Title: Modificação da molhabilidade de filmes carbono amorfo hidrogenado por processos ópticos
Other Titles: Wettability modification of hydrogenated amorphous carbon film by optical process
metadata.dc.creator: Ferreira, Leandro Lameirão
metadata.dc.contributor.advisor1: Zanon, Ricardo Antônio de Simone
metadata.dc.description.resumo: Este trabalho tem como objetivo investigar as mudanças na mol habilidade de filmes de carbono amorfo hidrogenado (a-C:H) induzidas por processos ópticos. Estes filmes de a-C:H foram depositados pela técnica química na fase vapor assistida por plasma (PECVD) sobre substratos de aço e latão, em ambiente com 100% de acetileno. Dois grupos de amostras foram preparados a fim de se estudar a influencia da radiação. O primeiro grupo foi depositado em diferentes temperaturas do substrato. O segundo em diferentes pressões de deposição. As amostras foram expostas a um largo espectro de energia, que se estendeu de UV a gama de alta e baixa atividades. A idéia por trás da exposição de radiação e investigar as mudanças na topografia das amostras como forma de avaliar as mudanças do caráter hidrofílico para hidrofóbico. Tipicamente, filmes de carbono amorfo hidrogenado são hidrofílicos em todas as condições estudadas. Este trabalho mostra que e possível fazer filmes de a-C:H menos hidrofílico usando tanto radiação gama quanto ultravioleta. Também, filmes de a-C:H podem alcançar estados hidrofóbicos induzidos por ultravioleta de alta energia, embora não seja permanente. Ainda, as amostras de a-C:H foram bombardeadas com íons de argônio a fim de investigar como as mudanças físicas influenciam a molhabilidade dos filmes. Os resultados mostram que a rugosidade induzida provoca o chamado efeito wicking que reforça o caráter de molhabilidade da superfície. Finalmente, todos os resultados apresentados neste trabalho mostram que o modelo de Wenzel pode ser aplicado para avaliar amostras de a-C:H crescidas conforme as condições aqui estudadas.
Abstract: This work investigates the wettability changes of hydrogenated amorphous carbon (a-C:H) induced by optical process. a-C:H films were grown by plasma enhanced chemical vapor deposition at 100% acetylene atmosphere. Steel and brass were used as substrates. Two groups of samples were prepared to study the radiation influence. First group was deposited at different substrate temperature and second one at different deposition pressure. Samples were exposed to radiation at different energy range, gamma and ultraviolet extend. The idea behind radiation exposure was to identify changes at the surface topography to evaluate changes at the hydrophilic/hydrophobic character of the samples. In essence, hydrogenated amorphous carbon films are hydrophilic at all conditions studied. This work shows it is possible to make a-C:H surfaces less hydrophilic using both gamma and ultraviolet radiation. Also samples can reach hydrophobic state induced by ultraviolet beam at high energy, although for a short period of time. Yet, samples were bombarded by argon ions in order to investigate how physical changes at the surface influence their wettability character. Results present the wicking effect, which says that induced roughness enhancement causes improvement of the wet character of the sample. In conclusion, all the results presented at this work suggest that Wenzel s model can be applied to evaluate a-C:H samples at the conditions here used.
Keywords: Carbono amorfo hidrogenado
Molhabilidade
Radiação gama
Radiação ultravioleta
Hydrogenated amorphous carbon
Wetting
Gamma radiation
Ultraviolet radiation
metadata.dc.subject.cnpq: CNPQ::CIENCIAS EXATAS E DA TERRA::FISICA
metadata.dc.language: por
metadata.dc.publisher.country: BR
Publisher: Universidade do Estado de Santa Catarina
metadata.dc.publisher.initials: UDESC
metadata.dc.publisher.department: Física
metadata.dc.publisher.program: Mestrado em Física
metadata.dc.rights: Acesso Aberto
URI: http://tede.udesc.br/handle/handle/1745
Issue Date: 24-Feb-2011
Appears in Collections:Mestrado em Física

Files in This Item:
File Description SizeFormat 
Arquivo 01.pdf241,61 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.