Título: Tratamento de envelhecimento artificial das ligas 356 e a 356: efeitos da composição química, do tempo e da temperatura nas propriedades mecânicas
Título(s) alternativo(s): Artificial aging heat treatment of 356 and A356 aluminum alloy: effect of chemical composition, time and temperature on the mechanical properties
Autor: Ronsani, Greice Scarduelli
Primeiro orientador: Verran, Guilherme Ourique
Resumo: Este trabalho avalia o efeito da composição química e do tratamento térmico de envelhecimento sobre as propriedades mecânicas da liga de alumínio 356. As variáveis estudadas foram o teor de magnésio, o tempo e a temperatura de tratamento térmico. Adicionalmente, os efeitos de elementos de liga presentes como o Fe e o Mn também foram avaliados, através da comparação com a liga A356 que é a versão mais pura da liga 356.0. Para a liga 356, dois percentuais de magnésio foram utilizados, 0,3% e 0,5% em peso e a liga foi denominada 356 baixo Mg e 356 alto Mg respectivamente.Os corpos de prova foram tratados a temperatura constante e tempos variados e após análises de resistência mecânica foram fundidos mais corpos de prova que foram tratados a temperatura constante, variando o tempo.Além dos ensaios de tração, outras técnicas foram usadas para avaliar o material.Ensaios de microdureza, microscopia óptica e eletrônica de varredura com análises pontuais EDX foram utilizadas.Comparando as ligas com baixo e alto teor de magnésio foram observadas variações significativas nas propriedades mecânicas.Além desta variável, o tempo e a temperatura de tratamento térmico também causaram variações nas propriedades mecânicas.A altas temperaturas pode ser observado o possível efeito de superenvelhecimento, onde uma queda na resistência mecânica foi observada.Nas análises microestruturais da liga 356 pode se perceber a presença de intermetálicos ricos em ferro e o mesmo não foi encontrado quando foi avaliada a microestrutura da liga A356.As propriedades mecânicas da liga A356 apresentaram valores menores do que aqueles obtidos para as propriedades mecânicas das ligas 356.Este fato pode ser relacionado com a presença de elementos endurecedores como o cobre e outros elementos de liga como o ferro e o manganês presentes na liga 356.
Abstract: This study evaluates the effect of chemical composition and heat treatment of aging on the mechanical properties of aluminum alloy 356. The variables of heat treatment were the magnesium content, time and temperature. Additionally, the effect of alloying elements present as Fe and Mn were also evaluated by comparing with the A356 which is the purest version of the 356.0 alloy. For alloy 356, two amount of magnesium were used, 0.3% and 0.5% in weight and the alloy was called the 356 low Mg and 356 high Mg, respectively.The samples were treated at constant temperature and varying times and after analysis of mechanical strength more specimens were cast that were treated at constant temperature, varying the time. In addition to tensile tests, other techniques were used to evaluate the material.Microhardness tests, optical microscopy and scanning electron microscopy analysis with point EDX were used.Comparing alloys with low and high magnesium content were observed significant variations in the mechanical properties .Besides this variable, the time and temperature of heat treatment also caused changes in the mechanical properties.At high temperatures can be observed the possible effect of over aging, where a decrease in mechanical strength was obsserved.In the microstructural analysis of the alloy 356 was noticed the presence of intermetallic iron-rich and the same was not found when we evaluated the microstructure of the alloy A356.As mechanical properties of A356 alloy showed values slightly lower than those obtained for the mechanical properties of alloys 356.This fact may be related to the presence of hardening elements such as copper and other alloying elements such as iron and manganese present in the alloy 356.
Palavras-chave: Metais
Tratamento Térmico de Ligas de Alumínio
Envelhecimento
Propriedades mecânicas
Magnésio
Heat treatment
Aluminum Alloys
Aging
Mechanical properties
Alloying elements
Área(s) do CNPq: CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Idioma: por
País: BR
Instituição: Universidade do Estado de Santa Catarina
Sigla da instituição: UDESC
Departamento: Ciência dos Materiais
Programa: Mestrado em Ciência e Engenharia de Materiais
Tipo de acesso: Acesso Aberto
URI: http://tede.udesc.br/handle/handle/1768
Data de defesa: 8-Jul-2010
Aparece nas coleções:Mestrado em Ciência e Engenharia de Materiais

Arquivos associados a este item:
Arquivo TamanhoFormato 
1 inicio-introducao.pdf80,24 kBAdobe PDFBaixar/Abrir Pré-Visualizar


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.