Título: Efeitos dos tratamentos de solubilização e precipitação sobre a microestrutura das ligas da família 356 com diferentes teores de magnésio
Título(s) alternativo(s): Effects of solubilization and precipitation treatment on microstructure of 356 family alloys with different leves of Mg.
Autor: Héllen Segundo, Elisa
Primeiro orientador: Verran, Guilherme Ourique
Resumo: Neste trabalho, foram investigados os efeitos dos tratamentos térmicos de solubilização e envelhecimento artificial (T6) sobre a microestrutura de ligas da família 356 (Al7Si0,3Mg) com diferentes teores de magnésio. Para caracterização dos resultados foram utilizados ensaios de microdureza e técnicas de microscopia ótica e eletrônica. Amostras fundidas da liga 356.0 com diferentes percentuais em peso (0,28%, 0,38% e 1% Mg) foram solubilizadas durante 10h a 540°C e submetidas a diferentes tempos e temperaturas de envelhecimento artificial. Os resultados dos ensaios de microdureza mostraram a ocorrência de incrementos nesta propriedade com o aumento de temperatura de envelhecimento e uma brusca queda nestes valores em amostras expostas a temperaturas mais elevadas (215°C). Com o intuito de identificar as alterações microestruturais associadas com estas variações nas propriedades mecânicas, bem como identificar os mecanismos envolvidos, foram realizadas analisadas via microscopia óptica (MO), eletrônica de varredura (MEV) e eletrônica de transmissão (MET). Com o uso de MO e MEV foi possível visualizar alterações significativas na microestrutura, no entanto os fenômenos microestruturais responsáveis pelo endurecimento por precipitação somente foram detectados usando MET. A utilização de microscopia eletrônica de transmissão permitiu observar a presença de nano precipitados responsáveis pela ocorrência de endurecimento por precipitação bem como dos precipitados incoerentes com a matriz que indicam a condição de superenvelhecimento.
Abstract: In this work, the heat treatment of solubilization and artificial aging effects (T6) on the microstructure of 356 alloys (Al7Si0,3Mg) with different magnesium content were investigated. The characterization was performed using microhardness tests and techniques of optical and electron microscopy. Samples of the casting alloy 356 with different percentages by weight (0.28%, 0.38% and 1% Mg) were solubilized for 10h at 540 ° C and subjected to different temperatures and times of artificial aging. The results of the microhardness test showed that the increase in mechanical properties is associated with increasing aging temperature and a sharp decrease in these values in samples exposed to higher temperatures (215 ° C). In order to identify the microstructural changes associated with these changes in mechanical properties and to identify the mechanisms involved, were carried out of the analyzed by optical microscopy, scanning eléctron (SEM) and transmission electronic (TEM). With the use of optical microscopy and SEM was possible to visualize significant changes in the microstructure, however the microstructural phenomena responsible by precipitation hardening were only detected using TEM. The use of transmission electron microscopy allowed to observe the presence of nano precipitated responsible for the occurrence of precipitation hardening and the incoherent precipitates with matrix indicate the condition of overaging
Palavras-chave: Ligas de alumínio 356.0
Fundição
Solubilização
Precipitação
356.0 aluminum alloys
Casting
Solubilization
Precipitation
Área(s) do CNPq: CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Idioma: por
País: BR
Instituição: Universidade do Estado de Santa Catarina
Sigla da instituição: UDESC
Departamento: Ciência dos Materiais
Programa: Mestrado em Ciência e Engenharia de Materiais
Tipo de acesso: Acesso Aberto
URI: http://tede.udesc.br/handle/handle/1680
Data de defesa: 28-Fev-2015
Aparece nas coleções:Mestrado em Ciência e Engenharia de Materiais

Arquivos associados a este item:
Arquivo TamanhoFormato 
Elisa Helen Segundo.pdf2,62 MBAdobe PDFBaixar/Abrir Pré-Visualizar


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.