Título: Nanocompósitos de PLLA com nanotubos de carbonos: propriedades mecânicas, tribológicas e térmicas
Título(s) alternativo(s): Nanocomposites PLLA with carbon nanotubes: mechanical, tribological and thermal properties
Autor: Bertholdi, Jonas
Primeiro orientador: Coelho, Luiz Antonio Ferreira
Resumo: Neste trabalho produziu-se nanocompósitos de PLLA com 0,25% e 0,50% (m/m) de nanotubos de carbono de paredes múltiplas (NCPM). A dispersão dos NCPM foi feita em solução de duas maneiras distintas, sendo uma utilizando sonificação de alta energia e outra sem. Avaliou-se o módulo de elasticidade por nanoindentação, o comportamento térmico por calorimetria exploratória e pela análise termogravimetria e as propriedades tribológicas dos nanocompósitos e do polímero puro através do ensaio de pino sobre disco com cargas de 5 e 10N. Pode-se observar uma queda de 4,2% no módulo de elasticidade no PLLA puro produzido com a sonificação. Os maiores aumentos no módulo foram obtidos com a concentração de 0,25% (5,4% e 6,7% para as sem sonificação e com sonificação). A microdureza apresenta um aumento até 18% para a amostra com 0,50%, independente do tratamento. Também se apresentam os resultados obtidos pela nanodureza que diferem dos obtidos da microdureza. A amostra com 0,25% obteve o menor volume removido na maioria das condições testadas no ensaio pino e disco. O coeficiente de atrito apresentou grande dispersão permitindo somente analisar as suas tendências. Os mecanismos de desgaste observados, adesão e abrasão, variam de intensidade com a incorporação de NCPM. Há indícios que a sonificação faz com que parte do material removido seja através do desgaste triboquímico. A temperatura de transição vítrea não apresentou variações. Foi verificada uma redução progressiva na temperatura de início de degradação por análise termogravimétrica com a adição dos NCPM. Não foi notada uma variação significativa na cristalinidade com incorporação de NCPM.
Abstract: In this study PLLA nanocomposites have been produced with 0.25 and 0.50 (wt%) multiwall carbon nanotubes (MWCNT). The MWCNT were dispersed in solution using two different ways: with and without high energy sonication. The mechanical results were evaluated by means of nanoindentation and microhardness, the thermal results by differential scanning calorimetric, thermogravimetric analysis and the tribological results by pin-on-disc tests with two different normal loads (5 and 10N). It was observed a reduction of 4.2% in elastic modulus of neat PLLA produced by sonication. The largest increases in the modulus were obtained with a concentration of 0.25% (6.7% and 5.4% for sonication and without it). The microhardness showed an increase of 18% for the sample with 0.50%, regardless of treatment. It is also presented the results obtained by nanohardness which differ from microhardness. The sample with 0.25% had the lowest volume loss in most conditions tested in the pin-ondisk. Most of the samples, with normal load of 10N, showed a lower wear rate than the same sample with a load of 5N. The friction coefficient showed a high dispersion of data allowing only analyzes the trends. The wear mechanisms observed adhesion and abrasion, vary in their intensity after the addition of MWCNT. There is evidence that sonication causes a portion of the material to be removed through tribochemical wear. The glass transition temperature did not show variations. It was observed a progressive reduction in the onset temperature of degradation by thermogravimetric analysis with the incorporation of MWCNT. It was not obtained an increase in crystallinity with incorporation of MWCNT.
Palavras-chave: PLLA
Nanotubos de carbono
Nanocompósitos
Propriedades térmicas
Tribologia
Nanoindentação
PLLA
MWCNT
Nanocomposites
Thermal properties
Tribological
Nanoindentation
Área(s) do CNPq: CNPQ::ENGENHARIAS::ENGENHARIA QUIMICA::TECNOLOGIA QUIMICA::POLIMEROS
Idioma: por
País: BR
Instituição: Universidade do Estado de Santa Catarina
Sigla da instituição: UDESC
Departamento: Ciência dos Materiais
Programa: Mestrado em Ciência e Engenharia de Materiais
Tipo de acesso: Acesso Aberto
URI: http://tede.udesc.br/handle/handle/1606
Data de defesa: 17-Fev-2012
Aparece nas coleções:Mestrado em Ciência e Engenharia de Materiais

Arquivos associados a este item:
Arquivo TamanhoFormato 
Capitulo - 1.pdf88,27 kBAdobe PDFBaixar/Abrir Pré-Visualizar


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.